1. Features: soft, low density
2. Purpose: Production of insoles and insoles
3. Characteristics of original solution
Product name | Exterior | Viscosity | density(g/cm3) | Storage stability £¨20 OCthe following£© | Package |
SX-P-8066 | liquid or waxy | 1500¡«2000 | 1.16¡«1.18 | 6 months | 18Kg/bucket |
SX-I-6395 | Transparent liquid without foreign matter | 100¡«300 | 1.18¡«1.20 | 3 months | 20Kg/bucket |
4. Catalysts and auxiliaries
The adding amount of SX-C-003 is 250¡À20g/18Kg, the adding amount of water is 0~60g/18Kg, and the adding amount of hardener SX-E-001 is 0-500 g/18Kg.
5. Molding conditions and physical property values
Reactivity | Technical Parameters | project | physical value | experiment method |
Reference scale P+C/I | 100/50~55 | Sole molding density (g/cm3) | 0.40~0.45 | GB/T6638¡ª86 |
Operating temperature(oC) | 40~45/38~42 | hardness(A type) (C type) | 30~35 40~50 | GB/T3903¡ª4 |
milky white time(s) | 6~9 | Tensile Strength (MPa) | 5.5~6.5 | GB/T6344 |
rise time(s) | 35~47 | Elongation (%) | 450~550 | GB/T6344 |
free bubble density (g/cm3) | 0.14~0.18 | Tear strength (kn/m) | 20~25 | GB/T10808 |
Metal mold temperature (oC) | 50~55 |
|
|
|
Demold time (min) | 5.0~7.0 |
|
|
|
|
|
|
|
|
¡¤The mixing ratio is based on the optimal mixing ratio value, which will vary with the type and amount of pigment additives added.
¡¤Long-term storage of P-5013 will cause the internal components to stratify, so stir evenly after heating and dissolving before use.¡¤The density of free foam will vary depending on the season (temperature, humidity).
¡¤The demoulding time will increase as the thickness of the molded product increases.
¡¤The physical property data is obtained by testing a 6mm thick test piece.
¡¤The above data is for reference only, and the specific data is subject to actual operation. If you need other physical property indicators, please contact our company.