1. Characteristics: low density, high hardness
2. Purpose: Production of women¡¯s high-heeled shoe soles and imitation wood fashion shoe soles
3. Characteristics of original solution
Product name | Exterior | Viscosity | density(g/cm3) | Storage stability £¨20 OCthe following£© | Package |
SX-P-9588 | Milky white liquid or waxy | 600¡«900 | 1.16¡«1.18 | 6 months | 18Kg/bucket |
SX-I-9722D | Transparent liquid without foreign matter | 200¡«400 | 1.18¡«1.20 | 3 months | 20Kg/bucket |
4. Catalysts and auxiliaries
The adding amount of SX-C-003 is 240¡À10g/18Kg, the adding amount of water is 80-130g/18Kg, and the adding amount of hardener SX-E-001 is 0-1500 g/18Kg.
5. Molding conditions and physical property values
Reactivity | Technical Parameters | project | physical value | experiment method |
Reference scale P+C/I | 100/95~97 | Sole molding density(g/cm3) | 0.3~0.4 | GB/T6638¡ª86 |
Operating temperature (oC) | 39~43/38~42 | hardness(A type) (C type) | 80~93 85~97 | GB/T3903¡ª4 |
milky white time(s) | 6~9 | Tensile Strength (MPa) | 3.0~4.0 | GB/T6344 |
rise time (s) | 35~49 | Elongation (%) | 100~200 | GB/T6344 |
free bubble density (g/cm3) | 0.14~0.17 | Tear strength (kn/m) | 15~20 | GB/T10808 |
Metal mold temperature (oC) | 45~55 |
|
|
|
Demold time (min) | 5.0~7.0 |
|
|
|
|
|
|
|
|
¡¤ Long-term storage of P-9589 will cause the internal components to stratify, so stir evenly after heating and dissolving before use.
¡¤The density of free foam will vary depending on the season (temperature, humidity).
¡¤The demoulding time will increase as the thickness of the molded product increases.
¡¤The physical property data is obtained by testing a 6mm thick test piece.
¡¤The above data is for reference only, and the specific data is subject to actual operation. If you need other physical property indicators, please contact our company.